Synthesis and characterization of lanthanide orthothiophosphates: LaPS ₄

The single crystal structure of LaPS₄, (1), is reported. The space group is tetragonal, I4(1)/acd. Unit cell dimensions are a = 10.9641(3) Å and c = 19.4828(9) Å. The far infrared absorption and Raman spectra (100-600 cm^-1) are consistent with the PS43- groups being in a distorted tetrahedral geometry. The room temperature emission spectrum of LaPS₄ doped with Er³⁺ is also presented. Emission peaks at 529, 534, 549, and 554 nm were observed when the sample was excited at 492 nm. The compound reported here is isomorphous and isostructural to several other lanthanide orthothiophosphates.